자세한 제품 설명을 보시려면 품명을 클릭하세요.
| Feature | RTV 3140 | RTV 3145 | 3-1944HP | SE9186 | SE9186L | SE9187L | SE9168 | SE9184 | LDC7091 | DC7091 | 744 | 3-0115 |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Part | One | One | One | One | One | One | One | One | One | One | One | One |
| Color | clear to slightly hazy | Grey or Clear | Translucent | Translucent,White | Translucent,Black | White,Gray | Gray | White | Black,white,gray | Black,white,gray | White | Gray |
| Extrusion rate | g/minute 175(3mm orifice at 0.6MPa) | |||||||||||
| Viscosity | 34,400 | 12,000(5rpm) 53,000(0.5rpm) |
66,100 | 26,900 | 25,000 | 비흐름성 | 비흐름성 | 비흐름성 | 비흐름성 | 비흐름성 | 비흐름성 | |
| Specific Gravity (Cured) | 1.05 | 1.12 | 1 | 1.04 | 1.02 | 1 | 1.32 | 2.2 | 1.4 | 1.4 | 1.42 | 1.29 |
| Cure Type(상온, Cure) | 상온 | 상온 | 상온 FTF | 상온 FTF | 상온 FTF | 상온 | 상온 FTF | 상온경화 | 상온 | 상온 | 상온 | 상온 |
| Tack-Free Time at 25 ºC | 116 | 90 | 7 | 9 | 8 | 8 | 7 | 3 | 28 | 28 | 40 | 20-25 |
| Working Time at 25 ºC | NA | |||||||||||
| Cure Condition | 7 days | - 0.5mm hours 24 - 3.2mm hours 72 - 3.2mm days 7(Full) |
3-7 days | 1 days (@25C/50%RH) |
1 days (@25C/50%RH) |
3-7 days | 2 days | 2 days | 3-7 days | 3-7 days | 3-7 days | 1 days (@25C/50%RH) |
| Thermal Conductivity | - | 0.17 | - | - | 0.84 | |||||||
| Tensile Strength (psi)/(Mpa)/(kgf.cm2) |
434 | 6.9MPa | 200 psi | 335 | 232 | 362 psi | 535/3.6/36 | 460/3.2/32 | 2.5 MPa | 430/2.7/28 | 430/2.7/28 | 350 psi |
| Unprimed Adhesion - Lap Shear to Aluminum | 1MPa(Glass) | 1.5MPa (Glass) |
1.5MPa (PA66GF30/Al) |
1.5MPa (PA66GF30/Al) |
||||||||
| Durometer | A 31.6 | A50 | A32 | A19 | A24 | A17 | A44 | A74 | A37 | A32 | A35 | A50 |
| Elongation | 419 | 650 | 180 | 555 | 340 | 160 | 363 | 60 | 680 | 680 | 600 | 405 |
| Dielectric Strength | 15 | 20 | 23 | 23 | 20 | 26 | 20 | |||||
| Dielectric Constant@ 1kHz | ||||||||||||
| Volume Resistivity | 2.1 x 10 (14) | 6.00E+15 | 3.00E+15 | 8.00E+15 | 1.50E+15 | |||||||
| UL Flammability Classification | UL94 V-1 | 94 V-0 | 94-HB | 94-HB | 94 V-0 | 94 V-0 | UL94 V-1 | 94-HB | ||||
| Shelf life | 12 | 12 | 12 | 12 | 12 | 12 | 12 | 12 | 6 | 12 | 12 | 18 |
| Feature | EA-9189H | Q3-6611 | X3-1598 | 3-6876 | SE-1714 | 3-6265 HP | 3-6265 Thixotropic |
|---|---|---|---|---|---|---|---|
| Part | One | One | One | One | One | One | One |
| Color | White | Gray | Black | Black | Beige or Black | Black | Black |
| Extrusion rate | Nonflow | ||||||
| Viscosity | 비흐름성 | 87,000 | 86,550 | 41,300 | 58,800 | 1,070,000 | 968,000 |
| Specific Gravity (Cured) | 1.68 | 1.31 | 1.32 | 1.311 | 1.3 | 1.33 | 1.34 |
| Cure Type(상온, Cure) | 상온 | Cure | Cure | Cure | Cure | Cure | Cure |
| Tack-Free Time at 25 ºC | 2 | 40 | |||||
| Working Time at 25 ºC | |||||||
| Cure Condition | 72Hours | 125C @ 60 150C @ 30 |
125C @ 60 150C @ 30 |
100C @ 300 125C @ 60 150C @ 30 |
150C @ 30 | 100C @ 240 125C @ 25 150C @ 10 |
125C @ 60 |
| Thermal Conductivity | 0.88 | 0.32 | - | - | 0.3 | ||
| Tensile Strength (psi)/(Mpa)/(kgf.cm2) |
576 | - | - | 55Kg/cm2 | 73Kg/cm2 | 850 | 700 (4.8MPa) |
| Unprimed Adhesion - Lap Shear to Aluminum | 363 | 825 | 611 | ||||
| Durometer | A80 | A59 | - | A53 | A66 | A68 | A60 |
| Elongation | 60% | - | - | 255 | 230 | 275 | 165 |
| Dielectric Strength | 28 | - | 22 | - | 30 | 24 | 21 |
| Dielectric Constant@ 1kHz | |||||||
| Volume Resistivity | 3.30E+15 | 1.00E+15 | 4.70E+14 | ||||
| UL Flammability Classification | 94 V-0 | UL94 | - | - | - | ||
| Shelf life | 9 | 12 | 12 | 12 | 9 | 12 | 12 |